Small crack growth from notches under variable amplitude loading requires that crack opening stress be followed on a cycle by cycle basis and taken into account in making fatigue life predictions. The use of constant amplitude fatigue life data that ignores changes in crack opening stress due to high stress overloads in variable amplitude fatigue leads to non-conservative fatigue life predictions. Similarly fatigue life predictions based on small crack growth calculations for cracks growing from flaws in notches are non-conservative when constant amplitude crack growth data are used. These non-conservative predictions have, in both cases, been shown to be due to severe reductions in fatigue crack closure arising from large (overload or underload) cycles in a typical service load history.

In present paper, the process of joining aluminum alloy 6111T4 and steel HSLA340 sheets by self-piercing riveting (SPR) is studied. The rivet material properties were obtained by inverse modeling approach. Element erosion technique was adopted in the LS-DYNA/explicit analysis for the separation of upper sheet before the rivet penetrates into lower sheet. Maximum shear strain criterion was implemented for material failure after comparing several classic fracture criteria. LS-DYNA/implicit was used for springback analysis following the explicit riveting simulation. Large compressive residual stress was observed near frequent fatigue crack initiation sites, both around vicinity of middle inner wall of rivet shank and upper 6111T4 sheet.

Failure mode and fatigue behavior of dissimilar laser welds in lap-shear specimens of aluminum and copper sheets are investigated. Quasi-static tests and fatigue tests of laser-welded lap-shear specimens under different load ranges with the load ratio of 0.1 were conducted. Optical micrographs of the welds after the tests were examined to understand the failure modes of the specimens. For the specimens tested under quasi-static loading conditions, the micrograph indicates that the specimen failed through the fusion zone of the aluminum sheet. For the specimens tested under cyclic loading conditions, two types of failure modes were observed under different load ranges. One failure mode has a kinked crack initiating from the interfacial surface between the aluminum and copper sheets and growing into the aluminum fusion zone at an angle close to 90°.

Active regeneration systems for cleaning diesel exhaust can operate at extremely high temperatures up to 1000°C. The extremely high temperatures create a unique challenge for the design of regeneration structural components near their melting temperatures. In this paper, the preparation of the sheet specimens and the test set-up based on induction heating for sheet specimens are first presented. Tensile test data at room temperature, 500, 700, 900 and 1100°C are then presented. The yield strength and tensile strength were observed to decrease with decreasing strain rate in tests conducted at 900 and 1100°C but no strain rate dependence was observed in the elastic properties for tests conducted below 900°C. The stress-life relations for under cyclic loading at 700 and 1100°C with and without hold time are then investigated. The fatigue test data show that the hold time at the maximum stress strongly affects the stress-life relation at high temperatures.

Due to magnesium alloy's poor weldability, other joining techniques such as laser assisted self-piercing rivet (LSPR) are used for joining magnesium alloys. This research investigates the fatigue performance of LSPR for magnesium alloys including AZ31 and AM60. Tensile-shear and coach peel specimens for AZ31 and AM60 were fabricated and tested for understanding joint fatigue performance. A structural stress - life (S-N) method was used to develop the fatigue parameters from load-life test results. In order to validate this approach, test results from multijoint specimens were compared with the predicted fatigue results of these specimens using the structural stress method. The fatigue results predicted using the structural stress method correlate well with the test results.

Variable amplitude torsion, bending, and combined torsion and bending fatigue tests were performed on an axle shaft. The moment inputs used were taken from the respective history channels of a cable log skidder vehicle axle. Testing results indicated that combined variable amplitude loading lives were shorter than the lives of specimens subjected to bending or torsion alone. Calculations using strain rosette readings indicated that principle strains were most active around specific angles but also occurred with lesser magnitudes through a wider angular range. Over the course of a biaxial test, cyclic creep narrowly limited the angles and magnitudes of the principal strains. This limitation was not observed in the calculated principal stress behavior. Simple life predictions made on the measured strain gage histories were non-conservative in most cases.

Powder metal based copper steels have found increased use in automotive applications, an example being powder-forged connecting rods. A characterization study was conducted to determine the effects of carbon content and manganese sulphide addition on the mechanical properties and machinability of these materials. Steel powder mixes containing 2% Cu and various graphite contents, with and without a MnS addition were pressed, sintered and forged to full density. Forged samples were then tested for tensile properties, hardness and fatigue strength. Machinability was determined by measuring tool life during drilling tests. It was found that increasing the carbon content from 0.28 to 0.69% has little effect on fatigue properties of powder-forged copper steels although the tensile, strength increased as expected. The addition of manganese sulphide did not affect the mechanical properties measured, but was found to significantly improve the machinability.

Since the environment of vehicle operation is dynamic in nature, dynamic methods should be used in vehicle durability analysis. Due to the constraints in current computer resources, simulation of vehicle durability tests and structural fatigue life assessment need special approaches and efficient CAE tools. The purpose of this paper is to present an efficient methodology and a feasible vehicle dynamic durability analysis process. Two examples of structural durability analysis using transient dynamics are given. The examples show that vehicle stress analysis and fatigue life prediction using dynamic method is now feasible by employing the presented method and process.

Magnesium alloys are the lightest structural metal and recently attention has been focused on using them for structural automotive components. Fatigue and durability studies are essential in the design of these load-bearing components. In 2006, a large multinational research effort, Magnesium Front End Research & Development (MFERD), was launched involving researchers from Canada, China and the US. The MFERD project is intended to investigate the applicability of Mg alloys as lightweight materials for automotive body structures. The participating institutions in fatigue and durability studies were the University of Waterloo and Ryerson University from Canada, Institute of Metal Research (IMR) from China, and Mississippi State University, Westmorland, General Motors Corporation, Ford Motor Company and Chrysler Group LLC from the United States.

A main requirement for a satisfactory function and service life of a forged powder metal connecting rod is the fatigue strength. Fatigue strength mainly depends on design, material, microstructure, and surface condition. Much work has been accomplished to optimize these factors, but still a variety of surface defects such as localized porosity, roughness, oxide penetration, decarburization, etc., can be developed during manufacturing. These surface defects impact the fatigue strength in various ways. The impact of the decarburized layer depth on the fatigue life of a forged powder metal connecting rod is the focus of this work. Several connecting rods were submitted to a Weibull test at the same loading pattern. After the fatigue tests, the connecting rods were divided into groups with different decarburized layer depths. Both Maximum Likelihood Estimates (MLE) and Rank Regression (RR) techniques were used to analyze test results from all the groups obtained.

The fatigue strength of spot welds in a multi-spot-welded structure is one of the key issues of concern for achieving structural durability and optimum design in automobile industry. In this study, a global-local fatigue life prediction method is proposed to predict the fatigue life of spot welds in multi-spot-welded structures. In this method, the remote stress-strain field away from the spot-welds, calculated from a global coarse finite element model, is assumed to be acceptable, and is used to recover the stress-strain information of the spot-welds. To improve the accuracy of the remote stress-strain field, an “equivalent” spot weld element is also proposed. The method makes it feasible to predict the fatigue life of spot welds without constructing a detailed finite element model for each spot weld. The method will help reduce finite element model size and save time.

The influence of calcium treatment on the mechanical properties of a plain carbon steel (SAE 1050) was investigated. The mechanical properties investigated were tensile and impact strength, fatigue crack growth rate, and the fatigue threshold. Impact testing was conducted at both room temperature and at -40°C. Several heats of both calcium and non-calcium treated steel (SAE 1050) were tested in both the as hot-rolled condition and in the quenched and tempered condition (with a hardness level of HRC = 45). The results of this investigation show no significant difference in the tensile properties or room temperature impact properties between the calcium treated and the non-calcium treated steels. However, the impact strengths of calcium treated steels were slightly higher than that of non-calcium treated steels at -40°C.

Increased use of powder-forged connecting rods in the automotive industry prompted an investigation into the suitability of powders from different suppliers for this application. Specifications developed by North American users call for ultra clean powders to enhance machinability and fatigue life. Powders from four manufacturers were each blended with graphite and lubricant, then pressed, sintered and forged to full density. Metallographic samples were prepared and evaluated for inclusion content. In addition, the powders were mixed to the composition of connecting rods, (C - 0.5%, Cu - 2% and MnS - 0.3%), and were similarly pressed, sintered and forged. Test bars were machined from the forged discs. Uniaxial fatigue tests were performed in the tension-compression mode and strain-life curves were developed. It was determined that all powders examined were very clean and were comparable in their inclusion content.

Shot peening is a commonly used surface treatment process used to improve the fatigue life of aircraft, automotive and other highly stressed structural components. This improvement is attributed to the formation of compressive residual stress on the surface layer of the material by the impingement of spherical media (shot). The compressive residual stress usually decreases the tensile stress created in the component by “in service” external forces and therefore increases the fatigue strength of the part. To quantify the improvement resulting from shot peening, the fatigue behavior of powder-forged connecting rods and laboratory test bars from the base material (2% copper steel), both in the stress-free (unpeened) and surface treated (shot peened) condition were compared. The fatigue data were correlated with the residual stress generated at the surface. The stress magnitude and depth were determined using x-ray diffraction analysis.

Estimations of the elastic-plastic stress states at notches from elastic finite element results based on Neuber type of correction method have proven very useful for many engineering problems. While this approximation technique has been regularly used in simple fatigue analysis of components subjected to predominantly uniaxial loading, its extension into multiaxial cases has been limited to monotonic loading. This paper presents a technique which integrates the Neuber type of correction method with a three-dimensional cyclic stress-strain model. Three major elements are involved: 1) an assumed elastic-plastic loading path; 2) a one-to-one relationship between the given elastic and the corrected elastic-plastic loading history; and 3) a plasticity model for multiaxial cyclic stress-strain analysis. The technique is then illustrated to be capable of estimating complex yet stable cyclic stress and strain histories at a notch.

A highly adaptable fatigue testing computer system is presented for controlling single or multichannel test machines. The system imposes most common varieties of waveforms and also provides time synchronization between channels, such as in the case of variable amplitude biaxial load histories, and monitors various feedback signals for both data acquisition and alarm purposes. The program operates in a real-time Unix system as a separate stand-alone process. Communication with other users or the operator is done only through a reserved common block of shared memory. This feature allows control and monitoring of all tests over the computer network. A user can simply login remotely and check the test or start a data acquisition task from any workstation in the company, and then take the data files and analyze them on other computers. This paper describes the operation of the software, the methodology behind the hardware selection and the software structure.

The cyclic behavior of single overlap aluminum joints joined through a number of different methods has been investigated using Alcan 5754-O, an alloy that potentially could be used in structural applications. Overlap shear tests of spot welded, clinched and riveted joints are compared on the basis of their fatigue performance. The fatigue response of the spot welded joint was the baseline to which the other fasteners were compared. Test results showed an improvement of approximately 25% for both the mechanical clinch joints and aluminum rivets in fatigue strength at 106 cycles. The most significant improvement in fatigue strength of 100% was found for the self piercing rivets at 106 cycles. The failure behavior of the various joining methods is discussed as well as the surface appearance.

Due to several indeterminate factors, the assessment of the durability performance of a vehicle body is traditionally accomplished using test methods. An analytical fatigue life prediction method (four-step durability process) that relies mainly on numerical techniques is described in this paper. The four steps comprising this process include the identification of high stress regions, recognizing the critical load types, determining the critical road events and calculation of fatigue life. In addition to utilizing a general purpose finite element analysis software for the application of the Inertia Relief technique and a previously developed fatigue analysis program, two customized programs have been developed to streamline the process into an integrated, user-friendly tool. The process is demonstrated using a full body, finite element model.

Fatigue analysis using finite element models of a full vehicle body structure subjected to proving ground durability loads is a very complex task. The current paper presents an analytical procedure for fatigue life predictions of full body structures based on a time-domain approach. The paper addresses those situations where this kind of analysis is necessary. It also discusses the major factors (e.g., stress equivalencing procedure, cycle counting method, event lumping and load interactions) which affect fatigue life predictions in the procedure. A comparison study is conducted which explores the combination of these factors favorable for realistic fatigue life prediction. The concepts are demonstrated using a body system model of production size.

Automotive product development requires higher degree of quality upfront engineering, faster CAE turn-around, and integration with other functional requirements. Prediction of potential durability concerns using analytical methods for sheet metal structures subjected to road loads and other customer uses has become very important. A process has been developed to provide design direction based upon peak loads, simultaneous peak loads, and vehicle program analytical or measured loads. It identifies critical loads at each input location and load sets for multiple input locations, filters load time histories, selects critical areas and analyzes for fatigue life. Several case studies have been completed. The results show that the variations are consistent with the accuracies in finite element analysis, road load data acquisition, and fatigue calculation methods.