THE PURPOSE of this experiment was to determine the role of residual stresses in fatigue strength independent of other factors usually involved when residual stresses are introduced. It consisted of an investigation of the influence of residual stresses introduced by shotpeening on the fatigue strength of steel (Rockwell C hardness 48) in unidirectional bending. Residual stresses were varied by peening under various conditions of applied strain. This process introduced substantially the same amount and kind of surface cold working with residual stresses varying over a wide range of values. It was found that shotpeening of steel of this hardness is beneficial primarily because of the nature of the macro-residual-stresses introduced by the process. There is no gain attributable to “strain-hardening” for this material. An effort was made to explain the results on the basis of three failure criteria: distortion energy, maximum shear stress, and maximum stress.*

The strain-life approach is now commonly used for fatigue life analysis and predictions in the ground vehicle industry. This approach requires the use of material properties obtained from strain-controlled uniaxial fatigue tests. These properties include fatigue strength coefficient (σf′), fatigue strength exponent (b), fatigue ductility coefficient (εf′), fatigue ductility exponent (c), cyclic strength coefficient (K′), and cyclic strain hardening exponent (n′). To obtain the aforementioned properties for the material, raw data from stable cyclic stress-strain loops are fitted in log-log scale. These data include total, elastic and plastic strain amplitudes, stress amplitude, and fatigue life. Values of the low cycle fatigue properties (σf′, b, εf′, c) determined from the raw data depend on the method of measurement and fitting. This paper examines the merits and influence of using different measurement and fitting methods on the obtained properties.

The recent development of TiAl-based alloys by the aerospace community has provided an excellent material alternative for hot components in automotive engines. The low density combined with an elevated temperature strength similar to that of Ni-base superalloys make TiAl-based alloys very attractive for exhaust valve applications. Lighter weight valvetrain components improve performance and permit the use of lower valve spring loads which reduce noise and friction and enhance fuel economy. However, difficult fabricability and a perception that TiAl alloys are high cost, low volume aerospace materials must be overcome in order to permit consideration for use in high-volume automotive applications. This paper provides a comparison of properties for several exhaust valve alternative materials. The density of TiAl alloys is lower than Ti alloys with creep and fatigue properties equivalent to IN-751, a current high performance exhaust valve material.

Speciation of sulfurous acid, sulfuric acid and ammonium sulfate collected from the aerosol phase on a Fluoropore filter has been readily accomplished using techniques of chemical ionization mass spectrometry combined with thermal separation. Thermal separation of ammonium hydrogen sulfate from ammonium sulfate was not possible. Spectral separation of these species by selective ionization is proposed. Analysis of sulfate aerosols collected from ambient air and catalyzed vehicle emissions is described. It was found that sulfuric acid aerosol was rapidly converted to ammonium sulfate or ammonium hydrogen sulfate in the presence of ambient concentrations of ammonia. Ambient samples collected in the Detroit metropolitan area have been found to contain only trace quantities of sulfuric aicd. Sulfate samples collected from a dilution tube into which catalyzed vehicle exhaust was injected were found to contain significant quantities of ammonium sulfate in addition to sulfuric acid.

Gas carburized and quenched low alloy steels typically produce surface microstructures which contain martensite, retained austenite and often NMTP's (non-martensitic transformation products). The NMTP's are caused by a reduction of surface hardenability in the carburizing process from loss of alloying elements to oxidation. Gas carburized low alloy steels such as SAE 8620 with NMTP's on the surface have been shown to have inferior bending fatigue properties when compared to more highly alloyed steels which do not form NMTP's, such as SAE 4615M. One method of minimizing the formation of oxides and eliminating NMTP formation during carburizing and quenching is to use plasma carburizing instead of conventional gas carburizing. In this study the microstructures and bending fatigue performance of plasma carburized SAE 8620 and SAE 4615M is compared to the same alloys conventionally gas carburized and quenched.

This paper discusses a motor vehicle noise source identification technique designed for use during the SAE J986a or similar drive-by test procedure. It provides, by application of the Fourier Transform, the capability to obtain a narrowband (9.8 Hz) frequency resolution over an extended frequency range (0-10,000 Hz) at the peak vehicle noise level, a particular RPM, or a particular vehicle location in the test zone. Other features include corrections for the Doppler shift, averaging of noise tests, and subtraction of spectra of two separate noise tests from a component disconnect/reconnect procedure. The above analysis, in conjunction with the noise source isolation resulting directly from the disconnect procedure, identifies the major vehicle noise contributors in terms of their respective amplitudes and frequencies.

Erosion damage to automotive car bodies caused by stones and small sand particles and road debris significantly affects the appearance of paint. Painted engineering plastics as well as precoated sheet steel are affected by erosion phenomenon. Erosion of painted plastic substrates results in cosmetic concerns while that on metal substrates results in cosmetic to perforation corrosion. This work describes a laboratory simulation of erosion of painted plastic substrates by small particles on various paint and substrate types. Gloss loss was used to quantitatively evaluate erosion of painted surfaces. Wear behavior of painted plastic substrates to slag sand impact was evaluated as a function of several variables including paint type (one-component melamine crosslinked (1K) vs. two-component isocyanate crosslinked (2K)), thermal history, and coating modulus. The effect of slag sand type (particle size and chemical composition) was studied.

Compositional and microstructural variations in a casting can often result in rather significant variations in the response to a given aging treatment, leading to location dependent mechanical properties. The objective of this study is to determine the effect of copper content and solidification rate on the aging behavior of a type 319 cast aluminum alloy. The nominal composition of the alloy is Al-7% Si-3.5% Cu-0.25% Mg, however, typical secondary 319 aluminum specifications allow copper levels to vary from 3-4%. Solidification rates throughout a casting can vary greatly due to, among other factors, differences in section size. To determine the effect of copper level and solidification rate on the aging response, aging curves were experimentally developed for this alloy. Three different copper levels (3, 3.5, 4%) and two solidification rates were used for this study. Aging temperatures ranged from 150-290°C with nine aging times at each temperature.

The presence of a foreign substance on or within a polymer often affects the mechanical, chemical and thermal properties of the material. The change in strength and rigidity of a polymer resulting from the plasticizing action of a sorbed chemical or due to the withdrawal of an added plasticizer by the leaching operation can seriously affect the useful life of the material. In the real engineering world, incompatible chemicals and lubricants get onto various plastic components unexpectedly through design, manufacturing processes, customers services and repairs. This paper presents a number of case-studies which illustrate how undesirable chemicals found on plastic parts can affect product performance and cause damage to the parts.

APPLICATIONS of nuclear energy in automotive manufacture have been made principally in the field of radioactivity. These are grouped under the following categories: radiography, nondestructive testing, gaging and control, tracer techniques, and static neutralizers. Radioactivity techniques are being used in foundry operations to check stock and metal levels in cupolas and distribution of element additives. In steel operations, these techniques are being used to check assimilation of ore-concentrate fines and thickness of rolled sheet steel. Other applications include measurement of pipe and wall thickness in pressure lines and engines, and inspection of castings and welds for internal faults. Radioactive techniques for improving processes, quality, and materials have potentially universal application. Greater industrial access to reactors will permit broader study and speed the development of new applications of radio-activity in industry.

Many foams exhibit significant strain rate dependency in their mechanical responses. To characterize these foams, a strain rate dependent constitutive model is formulated and implemented in an explicit dynamic finite element code developed at FORD. The constitutive model is developed in conjunction with a Lagrangian eight node solid element with twenty four degrees of freedom. The constitutive model has been used to model foams in a number crash analysis problems. Results obtained from the analyses are compared to the experimental data. Evidently, numerical results show excellent agreement with the experimental data.

Increased use of powder-forged connecting rods in the automotive industry prompted an investigation into the suitability of powders from different suppliers for this application. Specifications developed by North American users call for ultra clean powders to enhance machinability and fatigue life. Powders from four manufacturers were each blended with graphite and lubricant, then pressed, sintered and forged to full density. Metallographic samples were prepared and evaluated for inclusion content. In addition, the powders were mixed to the composition of connecting rods, (C - 0.5%, Cu - 2% and MnS - 0.3%), and were similarly pressed, sintered and forged. Test bars were machined from the forged discs. Uniaxial fatigue tests were performed in the tension-compression mode and strain-life curves were developed. It was determined that all powders examined were very clean and were comparable in their inclusion content.

Motivated by a combination of increasing consumer demand for fuel efficient vehicles, more stringent greenhouse gas, and anticipated future Corporate Average Fuel Economy (CAFE) standards, automotive manufacturers are working to innovate in all areas of vehicle design to improve fuel efficiency. In addition to improving aerodynamics, enhancing internal combustion engines and transmission technologies, and developing alternative fuel vehicles, reducing vehicle weight by using lighter materials and/or higher strength materials has been identified as one of the strategies in future vehicle development. Weight reduction in vehicle components, subsystems and systems not only reduces the energy needed to overcome inertia forces but also triggers additional mass reduction elsewhere and enables mass reduction in full vehicle levels.

AMONG the many outstanding advantages of the shell molding process of casting crankshafts, as described here, are the following: 1. Manner in which entire process responds to a high degree of automation. 2. Close tolerances that can be maintained from casting to casting. 3. Raw sand requirements are reduced from 125 lb (previous method) to 20 lb. 4. Results in 70% reduction in weight of chips produced. 5. Resulting crankshafts have highest wear resistance and exceptional endurance. 6. Gives additional design leeway: Allowing the most efficient distribution of weight. Contributing to engine compactness by varying the casting contour to prevent potential interferences.

PROPER protection of metal parts operating as bearing surfaces, or in contact under relatively heavy loads, during the break-in period often means the difference between successful operation and failure. Various surface coatings have been investigated to discover which ones will give this protection. The authors discuss here three types of surface treatment for cast-iron and steel that do give superior wear and scuff resistance.

This report presents results of experiments to determine the effect of elevated temperature exposures on the mechanical properties of aluminum alloy materials. The two alloys studied, 5754 and 6111, are of the types which would be used in a stamped automobile structure and exterior panels. Yield strength, tensile strength, and total elongation are reported for a variety of test conditions. The material temperature exposures simulated a broad range of conditions which might be experienced during manufacturing operations such as adhesive curing and vehicle paint bake cycles. In addition, tests were conducted at temperatures to resemble in-service under-hood and under body (near the exhaust system) conditions. Materials were prestrained various amounts prior to temperature exposure to simulate metal forming processes. Results show that both materials react to temperature and aging times differently.

This paper proposes an approach to use ABS wheel speed sensor signals together with other vehicle state information from a brake control module to detect an unbalanced tire or tires in real-time. The proposed approach consists of two-stage algorithms that mix a qualitative method using band-pass filtering with a quantitative parameter identification using conditional least squares. This two-stage approach can improve the robustness of tire imbalance or imbalances. The proposed approach is verified through vehicle testing and the test results show the effectiveness of the approach.

Structural system identification was applied to small sample problems and to large automotive structures. The technique combines mass and stiffness matrices from a finite element model with experimental mode shapes and natural frequencies to produce improved mass and stiffness matrices. In numerical experiments on small problems the procedure enabled us to identify regions of original finite element models where changes of model parameters were required to bring finite element predictions into better agreement with exact results. Also, node point displacements were calculated for small structures subjected to time-dependent sinusoidal loads, and it was found that predictions of displacements from “improved” models were more accurate than original finite element model predictions when forcing frequencies were within the range of experimental frequencies used with structural system identification calculations.

Under a new program of quality control in the field of powder metallurgy automotive parts called quality assurance, the supplier is made a closer partner with the buyer to get a more dependable part that consistently meets all requirements and specifications. The quality assurance program consists of review of potential suppliers, contract negotiations, initial quality assurance surveys, and routine quality assurance surveys.

The constant challenge for automotive engineers to design vehicles with greater reliability at lower cost has brought powder metallurgy (P/M) to the foreground. This technology provides parts to or near net shape and results in savings of material, energy, capital equipment and floor space. This paper is an extension of SAE reports 850458 and 870133 and describes automotive powder metal components not previously identified. It should help engineers find cost effective applications early in the design stage so that P/M technology can be efficiently adopted. In addition, recent important technological developments in the P/M field applicable to automotive parts are highlighted. In particular, increased reliability achieved through SPC is stressed. A novel blending process is described whereby the alloying ingredients are “glued” to iron powder particles resulting in an increase in P/M quality through improved homogeneity.