The development of an optimized heat treatment schedule, with the aim of maximizing strength and relieving tensile residual stress, is important to prevent in-service cylinder distortion in Al alloy engine blocks containing cast-in gray iron liners. However, to effectively optimize the engine block heat treatment schedule, the current solutionizing parameters must be analyzed and compared to the as-cast condition to establish a baseline for residual stress relief. In this study, neutron diffraction was carried out to measure the residual stress along the aluminum cylinder bridge following solution heat treatment. The stresses were measured in the hoop, radial and axial orientations and compared to a previous measured as-cast (TSR) engine block. The results suggest that solution heat treatment using the current production parameters partially relieved tensile residual stress in the Al cylinder bridge, with stress relief being more effective near the bottom of the cylinder.

The demand for light weight vehicles continues to stimulate extensive research into the development of light weight casting alloys and optimization of their manufacturing processes. Of primary relevance are Aluminum (Al) and Magnesium (Mg) based alloys, which have successfully replaced selected iron based castings in automobiles. However, optimization of as-cast microstructure, processing and performance remains a challenge for some Al-based alloys. In this context, placement of chills in castings has been frequently used to locally manipulate the solidification conditions and microstructure of a casting. In this work, the effect of using an active copper chill on the residual strain profile of a sand-cast B319 aluminum alloy was investigated. Wedge-shaped castings were produced with three different cooling conditions: copper plate chill, copper pipe with cooling water and no chill (baseline).

In recent years, light weight components have been an area of significant importance in automotive design. This has led to the replacement of steel and cast iron with aluminum alloys for many automotive components. For instance, Al-Si alloys have successfully replaced nodular and gray cast iron in the production of large automotive components such as engine blocks. However, excessive residual strain along the cylinder bores of these engine blocks may result in cylinder distortion during engine operation. Therefore, in this study, neutron diffraction was used to evaluate residual strain along the aluminum cylinder bridge and the gray cast iron liners of distorted and undistorted engine blocks. The strains were measured in the hoop, radial, and axial orientations. The results suggest that the residual strain along the aluminum cylinder bridge of the distorted engine block was tensile for all three measured components.