Ultrasonic spot welding (USW) is a promising joining method for magnesium to steel to overcome the difficulties of fusion welding for these two materials with significant differences in melting temperatures. In a previous paper, the results of ultrasonic spot welding of magnesium to steel, with sonotrode engaged Mg piece, was presented. In this study, same material combination (0.8-mm-thick galvanized mild steel and 1.6-mm Mg AZ31B-H24) was used, but with sonotrode engaging steel piece. Various welding time, from 0.4 to 2.0 sec, were applied. Tensile lap-shear test, optical metallography, and scanning electron micrography were conducted for joint strength measurement and microstructural evaluation. The joint strength reached over 4.2 kN at 1.8 sec welding time. Mg-Zn eutectic was formed at the interface, indicating the interfacial temperature over 344°C. The study demonstrated USW to be a viable process for potential manufacturing of mixed-metal joints.

Ultrasonic spot welds were made between sheets of 0.8-mm-thick hot-dip-galvanized mild steel and 1.6-mm-thick AZ31B-H24. Lap-shear strengths of 3.0-4.2 kN were achieved with weld times of 0.3-1.2 s. Failure to achieve strong bonding of joints where the Zn coating was removed from the steel surface indicate that Zn is essential to the bonding mechanism. Microstructure characterization and microchemical analysis indicated temperatures at the AZ31-steel interfaces reached at least 344°C in less than 0.3 s. The elevated temperature conditions promoted annealing of the AZ31-H24 metal and chemical reactions between it and the Zn coating.

The friction and wear characteristics of three commercially-available, electrolytic coatings for aluminum engine cylinder bores were compared to those of cast iron liners. A Ni/SiC electrocomposite, a hard anodized treatment, and a Plasma Electrolytic Oxidation (PEO) coating were investigated. ASTM standard test method G133-95, non-firing test method, for linearly reciprocating sliding wear was modified to use segments of piston rings and cylinder liners. Tests were conducted using Mr. Goodwrench™ 5W30 as a lubricant at room temperature. The normal force was 150N, the reciprocating frequency was 15Hz, the stroke length was 8mm, and the test duration was 60 minutes. Kinetic friction coefficients ranged from 0.1 to 0.22, typical of boundary lubrication. The Ni/SiC and cast iron samples exhibited the lowest friction. The wear resistance of the Ni/SiC coating was superior to that of cast iron.

This paper presents on-going finite element modeling efforts of friction stir spot welding (FSSW) process using Abaqus/Explicit as a finite element solver. Three-dimensional coupled thermal-stress model was used to calculate thermo-mechanical response of FSSW process. Adaptive meshing and advection schemes, which makes it possible to maintain mesh quality under large deformations, is utilized to simulate the material flow and temperature distribution in FSSW process. The predicted overall deformation shape of the weld joint resembles that experimentally observed. Temperature and stress graphs in the radial direction as well as temperature-deformation distribution plots are presented.

Three dimensional fabrics have seen increasing use lately as composite reinforcements. Advantages over prepreg or chopped fiber processes can include cost, handling, consistent quality, impact behavior, and resistance to delamination [1]. To gain acceptance in the transportation industry it is imperative that properties including dynamic and fatigue behavior be designable. A Progressive Failure Analysis (PFA) was developed jointly by Alpha Star Corp and NASA to predict fatigue life of composites and determine their damage mechanisms so that the life could be extended. The title of this software package is GENOA™, and it was used to focus on the three dimensional fabric called 3WEAVE™ made by 3TEX, Inc. It was discovered through fatigue testing that void content greatly affected fatigue life for the 3D E-glass fabric reinforcing a polyurethane modified vinyl ester resin called Dion 9800 from Reichhold. This is a common characteristic for most structural materials.

Composite materials have the potential to reduce the overall cost and weight of automotive structures with the added benefit of being able to dissipate large amounts of impact energy by progressive crushing. To identify and quantify the energy absorbing mechanisms in composite materials, test methodologies were developed for conducting progressive crush tests on composite specimens that have simplified test geometries. The test method development focused on isolating the damage modes associated with the frond formation that occurs in dynamic testing of composite tubes. A new test fixture was designed to progressively crush composite plate specimens under quasi-static test conditions. Preliminary results are presented under a sufficient set of test conditions to validate the operation of the test fixture.

The objective of the research presented in this paper was to assess the influence of stamping process on crash response of UltraLight Steel Auto Body (ULSAB) [1] vehicle. Considered forming effects included thickness variations and plastic strain hardening imparted in the part forming process. The as-formed thickness and plastic strain for front crash parts were used as input data for vehicle crash analysis. Differences in structural performance between crash models with and without forming data were analyzed in order to determine the effects and feasibility of integration of forming processes and crash models.

Mixing controlled compression ignition, i.e., diesel engines are efficient and are likely to continue to be the primary means for movement of goods for many years. Low-net-carbon biofuels have the potential to significantly reduce the carbon footprint of diesel combustion and could have advantageous properties for combustion, such as high cetane number and reduced engine-out particle and NOx emissions. We developed a list of over 400 potential biomass-derived diesel blendstocks and populated a database with the properties and characteristics of these materials. Fuel properties were determined by measurement, model prediction, or literature review. Screening criteria were developed to determine if a blendstock met the basic requirements for handling in the diesel distribution system and use as a blend with conventional diesel. Criteria included cetane number ≥40, flashpoint ≥52°C, and boiling point or T90 ≤338°C.

Metal additive manufacturing has high potential to produce automobile parts, due to its shape flexibility and unique material properties. On the other hand, residual stress which is generated by rapid solidification causes deformation, cracks and failure under building process. To avoid these problems, understanding of internal residual stress distribution is necessary. However, from the view point of measureable area, conventional residual stress measurement methods such as strain gages and X-ray diffractometers, is limited to only the surface layer of the parts. Therefore, neutron which has a high penetration capability was chosen as a probe to measure internal residual stress in this research. By using time of flight neutron diffraction facility VULCAN at Oak Ridge National Laboratory, residual stress for mono-cylinder head, which were made of aluminum alloy, was measured non-distractively. From the result of precise measurement, interior stress distribution was visualized.

The heat treatment of steel parts is an essential step in the manufacturing of high-performance components for a variety of commercial and military products. Distortion in the size and shape of parts resulting from the heat treatment process is a pervasive manufacturing problem that causes higher finishing costs, excessive scrap and rework, long delivery times, and negative environmental impact. To date, techniques that have been developed to reduce or eliminate heat treatment distortion are largely based on experience and have been limited to trial and error. This presentation describes the philosophy and results of an ongoing collaborative project to develop a methodology and computer simulation capability to predict ferrous alloy component response (distortion, residual stress, and microstructure) to industrial heat treatment processes for automotive, truck, bearing, and aerospace applications.

Phosphorous in diesel exhaust is derived via engine oil consumption from the zinc dialkyldithiophosphate (ZDDP) oil additive used for engine wear control. Phosphorous present in the engine exhaust can react with an exhaust catalyst and cause loss of performance through masking or chemical reaction. The primary effect is loss of light-off or low temperature performance. Although the amount of ZDDP used in lube oil is being reduced, it appears that there may is a minimum level of ZDDP needed for engine durability. One of the ways of reducing the effects of the resulting phosphorous on catalysts might be to alter the chemical state of the phosphorous to a less damaging form or to develop catalysts which are more resistant to phosphorous poisoning. In this study, lube oil containing ZDDP was added at an accelerated rate through a variety of engine pathways to simulate various types of engine wear or oil disposal practices.

Increasing the strength of materials is effective in reducing weight and boosting structural part performance, but there are cases in where the residual strain generated during the process of manufacturing of high-strength materials results in a decline of durability. It is therefore important to understand how the residual strain in a manufactured component changes due to processing conditions. In the case of a connecting rod, because the strain load on the connecting rod rib sections is high, it is necessary to clearly understand the distribution of strain in the ribs. However, because residual strain is generally measured by using X-ray diffractometers or strain gauges, measurements are limited to the surface layer of the parts. Neutron beams, however, have a higher penetration depth than X-rays, allowing for strain measurement in the bulk material.

The computer-aided-design and analysis of a robust casting process requires the optimization of both mold filling and solidification. A number of commercial casting codes are available for modeling the fluid flow during mold filling and the heat transfer during solidification. The next generation casting process models will build on present capabilities to allow the prediction of microporosity and other defects and microstructure. This paper will discuss the issues involved in the development of next generation casting process models and present results from a computer model for microporosity prediction that is based on first principles, and will take into account alloy composition, alloy microstructure, the initial hydrogen content of the liquid alloy, and the resistance to inter-dendritic fluid flow to feed shrinkage.

Several standard methods exist for testing composites, metals and plastics in Mode I fracture. However, these standard test methods have limitations that disqualify them as candidates for testing certain automotive materials. In order to conduct successful fracture toughness tests with these automotive materials, a modified double cantilever beam testing geometry and associated new procedure have been developed. Both the test procedure and the data analysis have been fully documented in a draft standard. Representative SRIM composite, e-coat steel and epoxy were selected to develop and validate the testing procedure.

Microstructures and failure mechanisms of spot friction welds (SFW) in aluminum 5754 lap-shear specimens were investigated. In order to study the effect of tool geometry on the joint strength of spot friction welds, a concave tool and a flat tool were used. In order to understand the effect of tool penetration depth on the joint strength, spot friction welds were prepared with two different penetration depths for each tool. The results indicated that the concave tool produced slightly higher joint strength than the flat tool. The joint strength did not change for the two depths for the flat tool whereas the joint strength slightly increases as the penetration depth increases for the concave tool. The experimental results show that the failure mechanism is necking and shearing for the spot friction welds made by both tools. The failure was initiated and fractured through the upper sheet under the shoulder indentation near the crack tip.

Metal Compression Forming (MCF) is a variant of the squeeze casting process, in which molten metal is allowed to solidify under pressure in order to close porosity and form a sound part. However, the MCF process applies pressure on the entire mold face, thereby directing pressure on all regions of the casting and producing a uniformly sound part. The process is capable of producing parts with properties close to those of forgings, while retaining the near net shape, complexity in geometry, and relatively low cost of the casting process. The paper describes the casting process development involved in the production of an aluminum A357 alloy motor mount bracket, including the use of a filling and solidification model to design the gating and determine process parameters. Tensile properties of the component are presented and correlated with those of forged components.

The most significant obstacle to the widespread use of carbon-fiber-based composites by the automotive industry is the high cost of carbon fibers in comparison to other potential structural materials. Carbon fibers are currently produced by thermal pyrolysis of a polyacrylonitrile (PAN) precursor to obtain the desired properties. The most significant cost factors in the process are the high cost of precursors and the high capital equipment and energy costs in conversion to carbon fiber. The Department of Energy is supporting developmental efforts to reduce costs in both precursor production and conversion areas. This paper describes developments in the conversion process. Because of the unsuccessful results of manufacturing carbon fibers through their direct heating with microwave radiation (variable frequency microwave [VFM] and single frequency microwave [SFM] energy), new avenues were explored for this processing.

For internal combustion engines and industrial machinery, it is well recognized that the most cost-effective way of reducing energy consumption and extending service life is through lubricant development. This presentation summarizes our recent R&D achievements on developing a new class of candidate lubricants or oil additives ionic liquids (ILs). Features of ILs making them attractive for lubrication include high thermal stability, low vapor pressure, non-flammability, and intrinsic high polarity. When used as neat lubricants, selected ILs demonstrated lower friction under elastohydrodynamic lubrication and less wear at boundary lubrication benchmarked against fully-formulated engine oils in our bench tests. More encouragingly, a group of non-corrosive, oil-miscible ILs has recently been developed and demonstrated multiple additive functionalities including anti-wear and friction modifier when blended into hydrocarbon base oils.

We examine the effects on materials temperatures and engine efficiency via simulations of engines operating at temperatures which exceed the thermal limits of today’s materials. Potential focus areas include high-speed, high-load operation (in the fuel-enrichment zone) as well as conditions of selective cooling at lower speeds and loads. We focus on a light-duty DISI and a heavy-duty CI engine using GT-Power. Temperature distributions within the head, block, piston, and valves were obtained from 3D FEA simulations coupled with 1D GT-Power representations of the engine’s gas flow and combustion regions.

Carbon fiber composite use in automobiles and light trucks could dramatically reduce energy use and engine-out emissions. However, worldwide capacity of 28,000 tonnes per year of carbon fiber from polyacrylonitrile (PAN) and petroleum pitch could support limited automotive use. Production of high-volume, industrial-grade fiber from renewable and recycled polymers (lignin, recycled plastics, regenerated cellulosics) could meet automotive demand. Profiles of material volumes, carbon content, and melting points indicate several attractive candidates for production melt-spun carbon fiber feedstocks. Effects on the carbon fiber production cycle and its integration into automotive production are discussed.