Search Results

A significant amount of residual stresses can be developed in aluminum castings during heat treatment. This paper reports an experimental study of the residual stress distributions in aluminum castings after solution treatment and water quench. The residual stresses in aluminum castings are measured using both optical and resistance strain rosettes. The optical strain rosette technique was recently developed in conjunction with ring-core cutting method for residual stress measurement. The measured residual stresses from optical and resistance strain rosettes are compared with the results of X-ray and neutron diffraction measurements. The advantages and disadvantages of various measurement methods are discussed.

In this paper, the development of random vibration testing schedules for durability design verification of engine mounted products is presented, based on the equivalent fatigue damage concept and the 95th-percentile customer engine usage data for 150,000 miles. Development of the 95th-percentile customer usage profile is first discussed. Following that, the field engine excitation and engine duty cycle definition is introduced. By using a simplified transfer function of a single degree-of-freedom (SDOF) system subjected to a base excitation, the response acceleration and stress PSDs are related to the input excitation in PSD, which is the equivalent fatigue damage concept. Also, the narrow-band fatigue damage spectrum (FDS) is calculated in terms of the input excitation PSD based on the Miner linear damage rule, the Rayleigh statistical distribution for stress amplitude, a material's S-N curve, and the Miles approximate solution.

This particular study focuses on four specific gear steels: SAE 4320, SAE 8822, PS18, and 20MnCr5. Notched specimens are manufactured from the four materials. Three point bending experiments were conducted which include ultimate tests and fatigue tests. Part I is on ultimate test only. Part II will concentrate on fatigue testing. In order to see how the carburization affected the fatigue performance of these steels, a residual stress test was performed on one sample of each steel by mean of the incremental hole drilling method. The compressive stresses were found in all four steels with minimum and maximum stress approximately equal. This suggests that the residual stresses are biaxial in the carburized steel case. The difference between the maximum and minimum stresses is within 37% for all steels. The residual stress after the carburization process were found to be highest in the 4320 steel and SAE 8822, followed by PS 18 and then MnCr.

The paper studies the distributions of residual stresses in auto components after induction hardening. Three prototype parts are analyzed in this paper. Firstly, the temperature fields of the analyzed parts are quantitatively simulated during quenching by simulating surface heating to the austenitization temperature of the material. Secondly, the formation and states of the residual stresses are predicted. Therefore the distribution of residual stress is simulated and shows compressive stresses on the surface of components so that the strength can be improved. The simulated results by computer are compared with experimental results. The good comparison indicates that the results obtained by the FEA analysis are reliable. Thus, it can be concluded that the FEA (Finite element analysis) program is effectively developed to simulate heating and quenching processes and residual stresses distribution.

Automotive parking gears were tempered using three different tempering processes with a motive of determining the best tempering processes in terms of the properties of the heat treated samples. The three tempering processes compared in this study are Induction temper, Furnace temper and Magnetic core-flux temper. Torsion tests, Residual Stress tests and metallurgical analysis were done on the samples that were induction heat-treated and then tempered using one of the above mentioned three tempering processes. The resultant test data was used to draw conclusions on the performance of the tempering processes.