J469A: Zinc Die Casting Alloys - SAE International
Browse Standards J469_201712
Current STABILIZED 2017-12-20

Zinc Die Casting Alloys(STABILIZED Dec 2017) J469_201712

Because of the drastic chilling involved in die casting and the fact that the solid solubilities of both aluminum and copper in zinc change with temperature, these alloys are subject to some aging changes, one of which is a dimensional change. Both of the alloys undergo a slight shrinkage after casting, which at room temperature is about two-thirds complete in five weeks. It is possible to accelerate this shrinkage by a stabilizing anneal, after which no further changes occur. The recommended stabilizing anneal is 3 to 6 h at 100 °C (212 °F), or 5 to 10 h at 85 °C (185 °F), or 10 to 20 h at 70 °C (158 °F). The time in each case is measured from the time at which the castings reach the annealing temperature. The parts may be air cooled after annealing. Such a treatment will cause a shrinkage (0.0004 in per in) of about two-thirds of the total, and the remaining shrinkage will occur at room temperature during the subsequent few weeks. Stabilizing results in a decrease in dimensions of about 0.0005 in per in from the original size of the casting. Stabilizing is, of course, unnecessary if the machine or fitting operations can be delayed until the castings have aged five weeks at room temperature.
When exposed to stagnant moisture or condensation with limited access to oxygen, a nonuniform type of corrosion may occur on zinc die castings, which often results in the formation of a bulky film of white corrosion products. This may hinder the operation of such parts as automobile lock cylinders, fuel pumps, and carburetors, and in severe cases result in rather rapid loss of zinc. Various types of chromate films are available to satisfactorily overcome this condition.
The same electroplating or enameling procedure is used with both alloys. Organic finishes are quite variable in their ability to adhere well to zinc surfaces. The phosphate type of chemical pretreatment has received widest commercial utilization, and most zinc die castings which are to be finished with lacquers or enamels are phosphate pretreated. In general, a much wider selection of finishes can be used on pretreated die castings.
The relative merits of the two SAE alloys may be outlined as follows:
J469_201712
2017-12-20
Latest
Stabilized
J469_198901
1989-01-01
Historical
Reaffirmed

SAE MOBILUS

Subscribers can view annotate, and download all of SAE's content. Learn More »

Access SAE MOBILUS »

Members save up to 18% off list price.
Login to see discount.
Special Offer: J-Paks offers a customized subscription plan that lets you pay for just the documents that you need, when you need them.

Get Involved

Want to participate in updating this standard?

X