The thermal deflection associated with the conventional die heat treating procedure usually requires extra die grinding process to fine-tune the die surface. Due to the size of the production die, the grinding is time consuming and is not cost effective. The goal of the study is to develop a new die heat treating process utilizing the flexible laser heat treatment, which could serve the same purpose as the conventional die heat treating and avoid the thermal deflection. The unique look of the developed zebra pattern laser heat treating process is defined as the Zebra Line. The heat-treating parameters and processes were developed and calibrated to produce the laser heat treating on laboratory size dies, which were subjected to the die wear test in the laboratory condition. The USS HDGI 980 XG3TM steel was selected to be carried out on the developmental dies in the cyclic bend die wear test due to its high strength and coating characteristic.

Ultrasonic spot welding (USW) is a promising joining method for magnesium to steel to overcome the difficulties of fusion welding for these two materials with significant differences in melting temperatures. In a previous paper, the results of ultrasonic spot welding of magnesium to steel, with sonotrode engaged Mg piece, was presented. In this study, same material combination (0.8-mm-thick galvanized mild steel and 1.6-mm Mg AZ31B-H24) was used, but with sonotrode engaging steel piece. Various welding time, from 0.4 to 2.0 sec, were applied. Tensile lap-shear test, optical metallography, and scanning electron micrography were conducted for joint strength measurement and microstructural evaluation. The joint strength reached over 4.2 kN at 1.8 sec welding time. Mg-Zn eutectic was formed at the interface, indicating the interfacial temperature over 344°C. The study demonstrated USW to be a viable process for potential manufacturing of mixed-metal joints.

Ultrasonic spot welds were made between sheets of 0.8-mm-thick hot-dip-galvanized mild steel and 1.6-mm-thick AZ31B-H24. Lap-shear strengths of 3.0-4.2 kN were achieved with weld times of 0.3-1.2 s. Failure to achieve strong bonding of joints where the Zn coating was removed from the steel surface indicate that Zn is essential to the bonding mechanism. Microstructure characterization and microchemical analysis indicated temperatures at the AZ31-steel interfaces reached at least 344°C in less than 0.3 s. The elevated temperature conditions promoted annealing of the AZ31-H24 metal and chemical reactions between it and the Zn coating.

The friction and wear characteristics of three commercially-available, electrolytic coatings for aluminum engine cylinder bores were compared to those of cast iron liners. A Ni/SiC electrocomposite, a hard anodized treatment, and a Plasma Electrolytic Oxidation (PEO) coating were investigated. ASTM standard test method G133-95, non-firing test method, for linearly reciprocating sliding wear was modified to use segments of piston rings and cylinder liners. Tests were conducted using Mr. Goodwrench™ 5W30 as a lubricant at room temperature. The normal force was 150N, the reciprocating frequency was 15Hz, the stroke length was 8mm, and the test duration was 60 minutes. Kinetic friction coefficients ranged from 0.1 to 0.22, typical of boundary lubrication. The Ni/SiC and cast iron samples exhibited the lowest friction. The wear resistance of the Ni/SiC coating was superior to that of cast iron.

Commercially available Third Generation Advanced High Strength Steels (GEN3 AHSS) are qualified by automakers worldwide. With an excellent combination of strength and ductility, GEN3 AHSS are cold-formable and have shown potential to replace press hardenable steels (PHS) in structural applications. With overall formability equivalent to 590DP, U. S. Steel 980 GEN3 AHSS (980 XG3™ AHSS) may achieve cold-formed component geometries similar to those achieved by hot-formed PHS. Furthermore 980 GEN3 AHSS demonstrates a substantial increase in post-forming yield strength due to the combined effects of work-hardening and bake-hardening-thereby contributing strongly toward crash energy management performance. The technical challenges and attributes of cold-formed 980 GEN3 AHSS are explored in this paper for an automotive rear rail application (currently PHS), including: formability analysis, wrinkling elimination and springback compensation.

Edge flanging represents one of the forming modes employed in multistage forming, and advanced high strength steels (AHSS) are more prone to edge cracking during sheared edge flanging than the conventional high strength steels (HSS) and mild steels. The performance of the sheared edge in flanging operation depends on the remaining ductility of the material in the sheared edge after the work hardening (WH) and damage produced by blanking and subsequent forming operations. Therefore, it is important to analyze the effect of work hardening produced by blanking and subsequent forming operations prior to edge flanging on the edge flanging performance. In this study, the effect of different forming operation sequences prior to edge flanging on the edge flanging performance was analyzed for a dual phase 780 steel.

This paper presents a technological comparison of weldability and mechanical properties between a dual phase steel (DP) and an advanced high strength low alloy steel (AHSLA) used for automotive structural parts in order to demonstrate some unclear characteristics of each. Samples were spot welded and had their hardness and microstructure analyzed, also a shear test was applied on the weld button area. The edge stretchability was analyzed using hole expansion tests and tensile tests to determine the tensile and yield strength, anisotropic coefficients and total elongation. Data were used to estimate crash energy absorption. The results showed an AHSLA steel with higher than typical ductility. Finally, while DP showed improved stretchability, it was also concluded that such AHSLA could perform better bendability, drawability, flangeability and weldability.

Advanced high strength steels (AHSS) are widely used in the automotive industry for various applications especially for structural and safety parts. One of the concerns for AHSS in stamping operations is edge fracture originating from sheared blanked edges. This type of failure cannot be predicted by computer simulations using the conventional forming limit as the failure criterion. The reason for this is that edge damage produced by the blanking operation is not incorporated into the computer models to properly simulate the material edge formability. This study presents a method to evaluate edge damage in terms of the residual stress at the sheared edge produced by the blanking operation. The method uses the level and distribution of edge strain hardening (ESH) through the material thickness as an index to characterize the edge damage caused by the shearing operation.

Commercially available Generation 3 (GEN3) advanced high strength steels (AHSS) have inherent capability of replacing press hardened steels (PHS) using cold stamping processes. 980 GEN3 AHSS is a cold stampable steel with 980 MPa minimum tensile strength that exhibits an excellent combination of formability and strength. Hot forming of PHS requires elevated temperatures (> 800°C) to enable complex deep sections. 980 GEN3 AHSS presents similar formability as 590 DP material, allowing engineers to design complex geometries similar to PHS material; however, its cold formability provides implied potential process cost savings in automotive applications. The increase in post-forming yield strength of GEN3 AHSS due to work and bake hardening contributes strongly toward crash performance in energy absorption and intrusion resistance.

A methodology that enables two-dimensional strain field measurement in the vicinity of ductile rupture is described. Fully martensitic steel coupons were strained to fracture using a miniature tensile stage with custom data and image acquisition systems. Rupture initiated near the center of each coupon and progressed slowly toward the gage section edges. A state-of-the-art digital image correlation technique was used to compute the true strain field before rupture initiation and ahead of the resulting propagating macroscopic crack before final fracture occurred. True strains of the order of 95% were measured ahead of the crack at later stages of deformation.

The objective of the research presented in this paper was to assess the influence of stamping process on crash response of UltraLight Steel Auto Body (ULSAB) [1] vehicle. Considered forming effects included thickness variations and plastic strain hardening imparted in the part forming process. The as-formed thickness and plastic strain for front crash parts were used as input data for vehicle crash analysis. Differences in structural performance between crash models with and without forming data were analyzed in order to determine the effects and feasibility of integration of forming processes and crash models.

Third generation advanced high strength steels (3GAHSS) are increasingly used in automotive for light weighting and safety body structure components. However, high material strength usually introduces higher springback that affects the dimensional accuracy. The ability to accurately predict springback in simulations is very important to reduce time and cost in stamping tool and process design. In this work, tension and compression tests were performed and the results were implemented to generate Isotropic/Kinematic hardening (I/KH) material models on a 3GAHSS steel with 980 MPa minimum tensile strength. Systematic material model parametric studies and evaluations have been conducted. Case studies from full-scale industrial parts are provided and the predicted springback results are compared to the measured springback data. Key variables affecting the springback prediction accuracy are identified.

Magnesium alloys are not corrosion resistant in many applications and they require coating protection. In this study, we developed an electroless E-coating technique for magnesium alloys and discussed a cathodic E-coating deposition mechanism for the electroless E-coating process. This coating can be formed within a few seconds by dipping a magnesium alloy (i.e., AZ91D) in an E-coat bath without applying a current or voltage. The deposited electroless coat can offer good protection to the AZ91D magnesium alloy in 5 wt% NaCl corrosive solution as well as in a phosphating bath. The most interesting finding is that the electroless coating is not sensitive to local damage. No preferential corrosion attack occurred along the scratches made on the coating.

Today’s automotive industry is witnessing increasing applications of advanced high strength steels (AHSS) combined with innovative manufacturing techniques to satisfy fuel economy requirements of stringent environmental regulations. The integration of AHSS in novel automotive structure design has introduced huge advantages in mass reduction while maintaining their structural performances, yet several concerns have been raised for this relatively new family of steels. One of those concerns is their potentially high springback after forming, which can lead to geometrical deviation of the final product from its designed geometry and cause difficulties during assembly. From the perspective of accurate prediction, control and compensation of springback, further understanding on the effect of residual stress in AHSS parts is urged. In this work, the residual stress distribution in a 980GEN3 steel part after hydroforming is investigated via experimental and numerical approaches.

Metal additive manufacturing has high potential to produce automobile parts, due to its shape flexibility and unique material properties. On the other hand, residual stress which is generated by rapid solidification causes deformation, cracks and failure under building process. To avoid these problems, understanding of internal residual stress distribution is necessary. However, from the view point of measureable area, conventional residual stress measurement methods such as strain gages and X-ray diffractometers, is limited to only the surface layer of the parts. Therefore, neutron which has a high penetration capability was chosen as a probe to measure internal residual stress in this research. By using time of flight neutron diffraction facility VULCAN at Oak Ridge National Laboratory, residual stress for mono-cylinder head, which were made of aluminum alloy, was measured non-distractively. From the result of precise measurement, interior stress distribution was visualized.

Press hardenable ultra high strength steel (UHSS) is commonly used for automotive components to meet crash requirements with minimal mass addition to the vehicle. Press hardenable steel (PHS) is capable of forming complex geometries with deep sections since the forming takes place at elevated temperatures up to 900 degrees Celsius (in the Austenitic phase). This forming process is known as hot-stamping. The most commonly used PHS grade is often referred to as PHS1500. After hot-stamping, it is typically required to have a yield strength greater than 950 MPa and a tensile strength greater than 1300 MPa. Most automotive design and material engineers are familiar with PHS, the hot-stamping process, and their capabilities. What is less known is the capability of 3rd Generation advanced high strength steels (AHSS) which are cold stamped, also capable of forming complex geometry, and are now in the process of, or have recently completed, qualification at most automotive manufacturers.

The composition of New Generation Vehicles under the Partnership for a New Generation of Vehicles (PNGV) program is anticipated to be significantly different from the typical automobile available now on the market. A spreadsheet cost model of the automobile recycling infrastructure was developed to estimate the potential effects of New Generation Vehicles on the future economic viability of the recycling industry. On the one hand, the higher value of aluminum is likely to cause a positive impact on the three distinct players in the recycling industry, if some technical issues are overcome. On the other hand, the economic viability of the current recycling industry may be diminished by the substitution of composites.

Heat treated cast aluminum components like engine blocks and cylinder heads can develop significant amount of residual stress and distortion particularly with water quench. To incorporate the influence of residual stress and distortion in cast aluminum product design, a rapid simulation approach has been developed based on artificial neural network and component geometry characteristics. Multilayer feed-forward artificial neural network (ANN) models were trained and verified using FEA residual stress and distortion predictions together with part geometry information such as curvature, maximum dihedral angle, topologic features including node's neighbors, as well as quench parameters like quench temperature and quench media.

Laser welding of dissimilar metals such as Aluminum and Copper, which is required for Li-ion battery joining, is challenging due to the inevitable formation of the brittle and high electrical-resistant intermetallic compounds. Recent research has shown that by using a novel technology, called laser braze-welding, the Al-Cu intermetallics can be minimized to achieve superior mechanical and electrical joint performance. This paper investigates the robustness of the laser braze-welding process. Three product and process categories, i.e. choice of materials, joint configurations, and process conditions, are studied. It is found that in-process effects such as sample cleanness and shielding gas fluctuations have a minor influence on the process robustness. Furthermore, many pre-process effects, e.g. design changes such as multiple layers or anodized base material can be successfully welded by process adaption.

The heat treatment of steel parts is an essential step in the manufacturing of high-performance components for a variety of commercial and military products. Distortion in the size and shape of parts resulting from the heat treatment process is a pervasive manufacturing problem that causes higher finishing costs, excessive scrap and rework, long delivery times, and negative environmental impact. To date, techniques that have been developed to reduce or eliminate heat treatment distortion are largely based on experience and have been limited to trial and error. This presentation describes the philosophy and results of an ongoing collaborative project to develop a methodology and computer simulation capability to predict ferrous alloy component response (distortion, residual stress, and microstructure) to industrial heat treatment processes for automotive, truck, bearing, and aerospace applications.