Search Results

Hole expansion of a dual phase steel, DP600, was numerically investigated using a damage-based constitutive law to predict failure. The parameters governing void nucleation and coalescence were identified from an extensive review of the x-ray micro-tomography data available in the literature to ensure physically-sound predictions of damage evolution. A recently proposed technique to experimentally quantify work-hardening and damage in the shear-affected zone is incorporated into the damage model to enable fracture predictions of holes with sheared edges. Finite-element simulations of a hole expansion test with a conical punch were performed for both a punched and milled hole edge condition and the predicted hole expansion ratios are in very good agreement with the experiment values reported by several researchers.

The development and calibration of stress state-dependent failure criteria for advanced high-strength steel (AHSS) and aluminum alloys requires characterization under proportional loading conditions. Traditional tests to construct a forming limit diagram (FLD), such as Marciniak or Nakazima tests, are based upon identifying the onset of strain localization or a tensile instability (neck). However, the onset of localization is strongly dependent on the through-thickness strain gradient that can delay or suppress the formation of a tensile instability so that cracking may occur before localization. As a result, the material fracture limit becomes the effective forming limit in deformation modes with severe through-thickness strain gradients, and this is not considered in the traditional FLD. In this study, a novel bending test apparatus was developed based upon the VDA 238-100 specification to characterize fracture in plane strain bending using digital image correlation (DIC).

This paper presents the numerical validation of the impact response of a hot formed B-pillar component with tailored properties. A laboratory-scale B-pillar tool is considered with integral heating and cooling sections in an effort to locally control the cooling rate of an austenitized blank, thereby producing a part with tailored microstructures to potentially improve the impact response of these components. An instrumented falling-weight drop tower was used to impact the lab-scale B-pillars in a modified 3-point bend configuration to assess the difference between a component in the fully hardened (martensitic) state and a component with a tailored region (consisting of bainite and ferrite). Numerical models were developed using LS-DYNA to simulate the forming and thermal history of the part to estimate the final thickness and strain distributions as well as the predicted microstructures.

Residual stress prediction arising from manufacturing processes provides paramount information for the fatigue performance assessment of components subjected to cyclic loading. The determination of the material model to be applied in the numerical model should be taken carefully. This study focuses on the estimation of residual stresses generated after deep rolling of cast iron crankshafts. The researched literature on the field employs the available commercial material codes without closer consideration on their reverse loading capacities. To mitigate this gap, a single element model was used to compare potential material models with tensile-compression experiments. The best fit model was then applied to a previously developed crankshaft deep rolling numerical model. In order to confront the simulation outcomes, residual stresses were measured in two directions on real crankshaft specimens that passed through the same modeled deep rolling process.

In this study, a finite element software application (SORPAS®) is used to simulate the effect of pulsing on the expected weld thermal cycle during resistance spot welding (RSW). The predicted local cooling rates are used in combination with experimental observation to study the effect pulsing has on the microstructure and mechanical properties of Zn-coated DP600 AHSS (1.2mm thick) spot welds. Experimental observation of the weld microstructure was obtained by metallographic procedures and mechanical properties were determined by tensile shear testing. Microstructural changes in the weld metal and heat affect zone (HAZ) were characterized with respect to process parameters.

In this work, a new air hybrid engine is introduced in which two throttles are used to manage the engine load in three modes of operation i.e. braking, air motor, and conventional mode. The concept includes an air tank to store pressurized air during braking and rather than a fully variable valve timing (VVT) system, two throttles are utilized. Use of throttles can significantly reduce the complexity of air hybrid engines. The valves need three fixed timing schedules for the three modes of operation. To study this concept, for each mode, the results of engine simulations using GT-Power software are used to generate the operating maps. These maps show the maximum braking torque as well as maximum air motor torque in terms of air tank pressure and engine speed. Moreover, the resulting maps indicate the operating conditions under which each mode is more effective. Based on these maps, a power management strategy is developed to achieve improved fuel economy.

This study investigates the fundamental stiffness and damping properties of a self-damped pneumatic suspension system, based on both the experimental and analytical analyses. The pneumatic suspension system consists of a pneumatic cylinder and an accumulator that are connected by an orifice, where damping is realized by the gas flow resistance through the orifice. The nonlinear suspension system model is derived and also linearized for facilitating the properties characterization. An experimental setup is also developed for validating both the formulated nonlinear and linearized models. The comparisons between the measured data and simulation results demonstrate the validity of the models under the operating conditions considered. Two suspension property measures, namely equivalent stiffness coefficient and loss factor, are further formulated.

Many design problems are discovered often late in the development process, when design flexibility is limited. It is the art of the refinement engineers to find a solution to any unpredicted issues at this stage. The refinement process contains many hours of testing and requires many prototypes. Having an accurate experimental model of the system in this phase could reduce refinement time significantly. One of the areas that usually require refinement and tuning late in the design process is engine and body mounting systems. In this paper, we introduce a technique to optimize the mounting system of a vehicle for a given objective function using experimental/numerical analysis. To obtain an accurate model of the vehicle, we introduce an experimental procedure based upon the substructuring method. The method eliminates the need for any accurate finite element method of the vehicle. Experimental results of the implementation of this approach to a real vehicle are presented.

This paper examines the application of damage models in tube bending and subsequent hydroforming of AlMg3.5Mn aluminum alloy tubes. An in-house Gurson-based damage model, incorporated within LS-DYNA, has been used for the simulations. The applied damage model contains several void nucleation and growth parameters that must be determined for each material. A simpler straight tube hydroforming process was considered first to check the damage parameters and predicted ductility. Then the model was applied to a sequence of bending and hydroforming. The damage history from pre-bending was mapped to the hydroforming stage, to allow prediction of the overall ductility. The applied forming parameters in the simulation were based on data extracted during the experimental tests. Finally, the numerical results were compared to the experimental data.

A so-called damage percolation model is coupled with Gurson-based finite element (FE) approach in order to accommodate the high strain gradients and localized ductile damage. In doing so, void coalescence and final failure are suppressed in Gurson-based FE modeling while a measured second phase particle field is mapped onto the most damaged mesh area so that percolation modeling can be performed to capture ductile fracture in real sheet forming operations. It is revealed that void nucleation within particle clusters dominates ductile fracture in aluminum alloy sheet forming. Coalescence among several particle clusters triggered final failure of materials. A stretch flange forming is simulated with the coupled modeling.

This research examines the effect of endfeed on the thickness and strains during bending of steel tubes. The tubes were bent using an instrumented rotary draw tube bender and subsequently hydroformed into a diamond-profile outside corner fill die. DQAK tubes with an OD of 76.2 mm and a thickness of 1.55 mm were investigated. Endfeed during bending was found to have a significant effect on the thickness and strains within the tube after bending, and numerical models that were generated showed good agreement with the experimental data. It is shown how slight changes in thickness can cause localized failure during hydroforming, and how excessive die clearances can cause large strains in undesired areas.

This work presents comparisons of finite element model predictions of static and dynamic denting with experimental results. Panels were stamped from 0.81, 0.93 and 1.00mm AA6111-T4 and then paint-baked to produce representative automotive outer body panels. Each type of panel was statically and dynamically dented at three locations using a 25.4mm steel ball. Static denting was accomplished with incremental loading of 22.24N loads up to a maximum of 244.48N. Dynamic denting was accomplished by dropping the steel ball from heights ranging from 200mm to 1200mm. Multi-stage finite element analysis was performed using LS-DYNA1 and ABAQUS2 to predict the entire process of forming, spring-back, denting and final spring-back of the dented panels. The predicted results show good correlation with the experiments, but also highlight the sensitivity of the predictions to formulation of the finite element problem.

A cold worked and induction hardened SAE1045 steel component exhibited excessive distortion after cold working and straightening, as well as cracking during straightening after induction hardening. Since the problems occurred only in certain heats of electric furnace (EF) steel, in which nitrogen content can vary widely and in some cases be quite high, and never occurred for basic oxygen furnace (BOF) steel for which nitrogen contents are uniformly low it was suspected that the source of the problem was low temperature nitrogen strain aging in heats of EF steel with a high nitrogen content. The measured distortion and mechanical properties at various stages in the fabrication process showed that while nitrogen content had no significant effect on the hot rolled steel the component distortion and strength after cold working and after induction hardening increased with increasing nitrogen content.

This study was undertaken to examine the role of tool finish orientation on the drawing of zinc-coated steel sheets. Beads of average roughnesses of 0.1 μm and 0.2 μm, finished parallel to and perpendicular to sliding, were used in the drawbead test. Lubrication was provided by unblended base oils of 4.5, 30, and 285 mm2/s @ 40°C, used neat and with a boundary additive, 1% stearic acid. Three types of coated sheet (galvannealed, electrogalvanized, and hot-dip galvanized) were compared to bare AKDQ steel sheet. Results show that lubricant viscosity had the greatest effect on friction, while bead finish orientation and coating type influenced the nature of metal transfer and the galling of the strip. Mixed-film lubrication dominated with the medium and heavy lubricants, here contact area and friction were reduced with increasing lubricant viscosity.

The present work is aimed at investigating the tribological factors influencing the LDH test. The material used was AKDQ cold-rolled bare steel, 0.82mm thick. The investigated factors included: test speed (0.833, 4.167, 6.667, and 8.333 mm/s), lubricant viscosity (4.5, 7.0, and 12.5 mm2/s), punch roughness (0.033 and 0.144 μm Ra), and test temperature (25 and 50 °C). Test speed and lubricant viscosity form a variation of the numerator of the Stribeck curve's x-axis (ηV). With ηV increasing from 4 to 120 mm3/s2 friction decreased, resulting in a 0.5 mm higher LDH. Increasing the punch roughness decreased friction producing an increase of 0.25 mm in the LDH. There appears to be an optimum roughness -- at which the roughness features act as lubricant reservoirs but the asperities do not break through the lubricant film -- resulting in minimum friction, therefore, maximum LDH.

Hybrid electric vehicles (HEVs) are considered as the most commercial prospects new energy vehicles. Most HEVs have adopted Atkinson cycle engine as the main drive power. Atkinson cycle engine uses late intake valve closing (LIVC) to reduce pumping losses and compression work in part load operation. It can transform more heat energy to mechanical energy, improve engine thermal efficiency and decrease fuel consumption. In this paper, the investigations of Atkinson cycle converted from conventional Otto cycle gasoline engine have been carried out. First of all, high geometry compression ratio (CR) has been optimized through piston redesign from 10.5 to 13 in order to overcome the intrinsic drawback of Atkinson cycle in that combustion performance deteriorates due to the decline in the effective CR. Then, both intake and exhaust cam profile have been redesigned to meet the requirements of Atkinson cycle engine.

Due to the high power and energy density and also relative safety, lithium ion batteries are receiving increasing acceptability in industrial applications especially in transportation systems with electric traction such as electric vehicles and hybrid electric vehicles. In this regard, to ensure performance reliability, accurate modeling of calendar life of such batteries is a necessity. In fact, potential failure of Li-ion battery packs remains a barrier to commercialization. Battery pack life is a critical feature to warranty and maintenance planning for hybrid vehicles, and will require adaptive control systems to account for the loss in vehicle range, and loss in battery charge and discharge efficiency. Failure not only results in large replacement costs, but also potential safety concerns such as overheating or short circuiting which may lead to fires.

One of the major concerns preventing wider utilization of high strength steels (HSS) and advanced high strength steels (AHSS) in hydroforming is their inherent lower formability, compared to conventional mild steels. The application of the axial forces on the tube ends during a hydroforming operation is often referred to as end-feed, and can facilitate deformation of the tube by postponing failure. This research examines the effect of end-feed on the formability of HSS and AHSS tubes during hydroforming. Through simulation, straight and pre-bent tubes are hydroformed at different levels of end-feed for three materials: DDQ, HSLA350 and DP600.

The increased use of zinc coatings on steels has led to a decrease in their weldability. Weld current and time need to be increased in order to achieve sound welds on these materials compared to uncoated steels, and electrode tip life suffers greatly due to rapid alloying and degradation. In this work, typical uncoated Class II electrodes were tested along with a TiC metal matrix composite (MMC) coated electrode. Tests were conducted to study the weldability and process of nugget formation for both electrodes on HDG (hot dipped galvanized) HSLA (high strength low alloys) steels. Current and time ranges were constructed for both types of electrodes by varying either the weld current or weld time while holding all other parameters constant. Analysis of weld microstructures was conducted on cross-sectioned welds using SEM (scanning electron microscopy). Using the coated electrodes reduced weld current and times needed to form MWS (minimum weld size) on the coated steels.

Parameter identification of a math-based spark-ignition engine model is studied in this paper. Differential-algebraic equations governing the dynamic behavior of the engine combustion model are derived using a quasi-dimensional modelling scheme. The model is developed based on the two-zone combustion theory with turbulent flame propagation through the combustion chamber [1]. The system of equations includes physics-based equations combined with the semi-empirical Wiebe function. The GT-Power engine simulator software [2], a powerful tool for design and development of engines, is used to extract the reference data for the engine parameter identification. The models is GT-Power are calibrated and validated with experimental results; thus, acquired data from the software can be a reliable reference for engine validation purposes.